铝合金腐蚀的标准汇总（列表）

2025-05-19 17:38:23 作者：本网发布来源：网络分享至：

(1) ASTM G34-23 Standard test method for exfoliation corrosion（剥落腐蚀） susceptibility in 2XXX and 7XXX series Aluminum alloys(EXCO test)

(2) ASTM G47-22 Standard Test Method for Determining Susceptibility to Stress Corrosion Cracking（应力腐蚀开裂） of 2XXX and 7XXX Aluminum Alloy Products

(3) ASTM G66-23 Standard test method for visual assessment of exfoliation corrosion susceptibility of 5XXX series aluminum alloys(ASSET Test)

(4) ASTM G67-18 Standard test method for determining the susceptibility to intergranular corrosion（晶间腐蚀） of 5XXX series aluminum alloys by mass loss after exxposure to Nitric Acid(NAMLT Test)

(5) ASTM G69-20 Standard test method for measurement of corrosion potentials（腐蚀电位） of alluminum alloys

(6) ASTM G103-1997R23(e1) Standard practice for evaluating stress corrosion cracking resistance of low copper 7XXX series Al-Zn-Mg-Cu alloys in boiling 6% sodium chloride solution

(7) ASTM G110-92（2022）e2 Standrad practice for evaluating intergranular corrosion resistance of heat treable aluminum alloys by immersion in Sodium Chloride + Hydrogen Pereoxide solution

(8) ASTM G112-2022 Standard Gudie for conducting exfoliation corrosion tests in aluminum alloys

(9) ASTM G139-05（2022） Test Method for determining stress corrosion cracking resistance of heat-treable Aluminum Alloy products using Breaking Load method

(10) GB/T 7998-2005 铝合金晶间腐蚀测定方法（Test method for intergranular corrosion of aluminum alloy),参考ASTM G110-1992

(11) GB/T 7998-2023 铝合金晶间腐蚀敏感性评价方法（Method for evaluating the suscetibility to intergranular corrosion of alumunum alloys),替代GB/T 79998-2005he GB/T 26491-2011《5XXXX系铝合金晶间腐蚀试验方法质量损失法》，适用于2、5、6、7系铝合金产品晶间腐蚀敏感性的测定。

(12) GB/T 22640-2023 铝合金应力腐蚀敏感性评价试验方法（Test method for determining susceptibility to stress corrosion cracking of aluminum alloys)

适用于：C型环试样恒应变、弯梁试样恒应变、U型试样恒应变、拉伸试样恒载荷、拉伸试样恒应变、拉伸试样慢速率拉伸、沸腾氯化钠溶液恒应变等；（2系-Cu1.8%~7.0%、6系、7系-Cu0.4%~2.8%）

(13) GB/T 26323-2010 色漆和清漆铝及及合金表面涂膜的耐丝状腐蚀试验（Paints and varnishes - determination of resistance to filiform corrosion on aluminum and aluminum alloys( ISO 4623-2:2003 MOD)

(14) GB/T 33883-2017 7XXX系铝合金应力腐蚀沸腾氯化钠溶液法（铜含量低于1.2%）

(15) GB/T 36174-2018 金属和合金的腐蚀固溶热处理铝合金的耐晶间腐蚀性的测定（ ISO 11846:1995，IDT）

(16) GB/T 40388-2021 金属和合金的腐蚀铝合金剥落腐蚀试验（ISO 11881:1999，MOD）

(17) GB/T 41653-2022 金属和合金的腐蚀热处理铝合金晶间腐蚀敏感性阳极试验方法（ corrosion of metals and alloys - anodic test for evaluation of intergranular corrosion susceptibility of heat treatable aluminum alloys）ISO 15329:2006，MOD

(18) GB/T 42514-2023 铝及铝合金阳极氧化膜及有机聚合物膜的腐蚀评定图表法（ ISO 8993:2018，NEQ）

(19) GB/T 42544-2023 铝及铝合金阳极氧化膜及有机聚合物膜的腐蚀评定栅格法（ISO 8994:2018，NEQ）

(20) HB 5254-83 变形铝合金拉伸应力腐蚀试验方法

(21) HB 5255-83 铝合金晶间腐蚀及晶间腐蚀倾向的测定

(22) HB 5259-83 铝合金C环试样应力腐蚀试验方法

(23) HB 5294-84 高强度铝合金双悬臂（DCB）试样应力腐蚀试验方法

(24) MH/T 6071-2011 夹层腐蚀试验方法Test method for sandwich corrosion test

(25) SH/T 0620-95 发动机冷却液对传热状态下的铸铝合金腐蚀测定法（等效采用ASTM D4340）

(26) SJ 30046-2019 铝合金晶间腐蚀试验方法

(27) SJ 30047-2019 铝合金剥落腐蚀试验方法

(28) T/CCTAS 54-2023 轨道交通车辆用铝合金材料晶间腐蚀测定方法

(29) T/CCTAS 55-2023 轨道交通车辆用抗应力腐蚀铝合金材料过程控制要求